Hey if you want to give it a second go I have some 1/4 windows out of a 73 Super i'll give you for free if you pay shipping. What year is your car?
Posted: Wed Jul 27, 2005 7:22 am
by vdubyah73
try the cut and let it cool method just like welding weld a little let it cool.
Bill
Re: Tempered glass ....cut with a Plasma?
Posted: Wed Jul 21, 2010 7:10 pm
by greggholmes
Re: Tempered glass ....cut with a Plasma?
Posted: Sun Aug 01, 2010 2:48 pm
by earthquake
new guy here
I run a water jet where I work, I just want to add that you cant cut tempered glass with a water jet. it will usally go about 2 or 3 inches before it pops, I made it about 7 inches in to a sheet about 6' x 8' before it went, sounded like a gun shot.
Earthquake
Re: Tempered glass ....cut with a Plasma?
Posted: Wed Aug 04, 2010 12:19 pm
by Unkl Ian
Tempered Glass can't be cut.
Especially using a process that generated heat.
Re: Tempered glass ....cut with a Plasma?
Posted: Thu Aug 05, 2010 12:46 am
by Tom Notch
Well, sort of like my reply to whether a glass is 1/2 full or 1/2 empty.
You can cut the glass with an plasma arc........
you just may not like the size of the pieces....
Re: Tempered glass ....cut with a Plasma?
Posted: Fri Aug 06, 2010 5:56 am
by DWP
As a research Glassblower for over 30 years I need to explain.
DO Not Try It. You will get glass all over hells half acre. There might even be some blood.
Reason, glass when heated wants to expand. When the hot parts meets the cold part there is a lot of thermal stress. Something has to give. Ever try to melt a beer bottle with a torch?
The only way to use a flame on a piece of window glass is to slowly heat the entire piece up in a oven to at least 1000F. Melt the area you are working on and slowly cool down the entire piece in a oven. Even the "pyrex" glass I work needs to go through a oven to even out the stress.
If and that is a big IF you were able to melt a piece the stress left over WILL crack sooner or later.
Dave